 Post subject: Which solder??
PostPosted: Wed Jun 27, 2007 3:36 pm 
Offline
Friend
Friend
User avatar

Joined: Sun May 13, 2007 11:08 pm
Posts: 21
Which is the best solder to use?
I've got three types:
60 / 40 .032"
62/36/02 .032"
SN 100C lead free .032" here are the specs:

http://www.aimsolder.com/SN100C.cfm

bubblebloy


Top
 Profile  
 
 Post subject:
PostPosted: Wed Jun 27, 2007 4:23 pm 
Offline
Novice
Novice
User avatar

Joined: Mon Sep 18, 2006 8:15 am
Posts: 86
Location: Toronto
Can't go wrong with 60/40.

I've read 62/36 has an ideal melting point. So it might be easier to use. Apparently it cools as soon as you remove heat so you aren't slowly cooking your fingertips while you wait for the solder to harden.

Lead free is good if you handle A LOT of solder and don't like to wash your hands.

I can't comment on their tonal properties. But I'm sure there's someone out there who will tell you otherwise. :shock:


Top
 Profile  
 
 Post subject:
PostPosted: Wed Jun 27, 2007 8:00 pm 
Offline
Holy Ghost
Holy Ghost
User avatar

Joined: Sun Mar 13, 2005 4:10 pm
Posts: 7519
Location: Canada
I use AIM, SN 63/PB 37 Flux RA 3% .032" dia.

It works fine for me. I haven't tried the lead free type yet.

_________________
Stephen
Web: www.trinityamps.com. Facebook: facebook.com/trinityamps. Twitter: @trinityamps


Top
 Profile  
 
 Post subject:
PostPosted: Wed Jun 27, 2007 8:07 pm 
Offline
Friend
Friend
User avatar

Joined: Sun May 13, 2007 11:08 pm
Posts: 21
Can I use SN 100C?


Top
 Profile  
 
 Post subject:
PostPosted: Wed Jun 27, 2007 10:33 pm 
Offline
Holy Ghost
Holy Ghost
User avatar

Joined: Sun Mar 13, 2005 4:10 pm
Posts: 7519
Location: Canada
Yes. I'm sure it would work. Jsut check to see at what temp it melts and be sure your iron can deliver it.

_________________
Stephen
Web: www.trinityamps.com. Facebook: facebook.com/trinityamps. Twitter: @trinityamps


Top
 Profile  
 
 Post subject:
PostPosted: Thu Jun 28, 2007 4:06 pm 
Offline
Expert
Expert

Joined: Tue Sep 19, 2006 11:46 am
Posts: 1078
Location: PA
Hmmm,
Now I have to wonder.
I'm using Kester 66/44 .050?


Top
 Profile  
 
 Post subject:
PostPosted: Thu Jun 28, 2007 11:42 pm 
Offline
Novice
Novice

Joined: Thu May 17, 2007 9:18 pm
Posts: 61
my personal preference would be 62/36/02 .032 for extra conductivity but you also want be sure to have an iron that will be able to deliver the extra heat needed to melt it... if you look around you can find solder with an even higher silver content but again you will need an iron with the heat to melt it ( sorry didn't use spell check )



Bill

_________________
My future's so bright I gotta wear shades


Top
 Profile  
 
 Post subject:
PostPosted: Sun Jul 01, 2007 1:35 pm 
Offline
Friend
Friend
User avatar

Joined: Mon Jul 10, 2006 5:17 pm
Posts: 18
Solder without lead has a higher metling point so you have to heat it up more and it is possible to burn you component but that is a issue with a sensitive stuff(IC, small diodes,SMD and etc.)


Top
 Profile  
 
 Post subject:
PostPosted: Sun Jul 01, 2007 4:03 pm 
Offline
Friend
Friend
User avatar

Joined: Sun May 13, 2007 11:08 pm
Posts: 21
I tested the sn100c solder and I found that there was no problem in melting it (using a simple 30 watt iron) but I found that when the solder cooled it was "cloudy" in appearance and not bright and shiny as a good soldered joint should be.

bubbleboy


Top
 Profile  
 
 Post subject:
PostPosted: Sun Jul 01, 2007 4:49 pm 
Offline
Friend
Friend
User avatar

Joined: Sun May 13, 2007 11:08 pm
Posts: 21
SN100C solder has a melting point 227C and has better conductivity then tin/lead solders see article: http://cs.pennnet.com/Articles/Article_ ... =lead-free


Top
 Profile  
 
 Post subject:
PostPosted: Wed Jul 04, 2007 12:56 am 
Offline
Friend
Friend
User avatar

Joined: Thu Apr 27, 2006 4:06 pm
Posts: 22
Location: So. Calif.
What's "solder"?


Top
 Profile  
 
 Post subject:
PostPosted: Fri Apr 25, 2008 10:56 am 
Offline
Holy Ghost
Holy Ghost
User avatar

Joined: Sun Mar 13, 2005 4:10 pm
Posts: 7519
Location: Canada
is this a good topic for the reference forum?

_________________
Stephen
Web: www.trinityamps.com. Facebook: facebook.com/trinityamps. Twitter: @trinityamps


Top
 Profile  
 
 Post subject:
PostPosted: Fri Apr 25, 2008 12:45 pm 
Offline
Experienced
Experienced

Joined: Fri Mar 14, 2008 12:05 pm
Posts: 432
Location: Massachusetts
I am planning on covering this topic in greater detail for the "Resource" Forum in my Selecting Basic Tools and Materials tutorial. For now though I would agree with Stephen's choice of a tin/lead 63/37 with a 3.3% RMA or RA (non-corrosive only) flux core. A diameter of .031" is fine for all of the joint types found in a typical guitar amp build, although this may be too large for most PCB work if you mod effects pedals, etc. This is the preferred solder choice of the military because of it's proven track record, low melting point, excellent wetting, and a very fast transition from solid to liquid to solid, relatively easy to clean, oh, and looks good! Unless your country requires the use of a lead free solder (or you ship product to a country that does), I would tend to shy away from the current lead free products. Substantially higher melting point, dull grey and pitted finish, special soldering iron and soldering tips, etc. To me it's a not ready for prime time product right now to satisfy the tree huggers of the world!

I have so much info to share on this subject (clean/no clean solders, flux choices, water soluble fluxes, cleaning methods, etc.) that can be covered in as great a length as this forum desires, but time is a very frustrating issue for me right now. For now I would suggest sticking with the military's choice, which after all created most or all of the 50's build technology that you are all building and enjoying today! I can also field specific questions if you ever want to PM me directly. I'm happy to help.

BTW: I've never worked with silver solder products so I can't comment on them without a little research.

Joe G

_________________
Some assembly required,
Brain sold separately...


Top
 Profile  
 
 Post subject:
PostPosted: Fri Apr 25, 2008 1:15 pm 
Offline
Holy Ghost
Holy Ghost
User avatar

Joined: Sun Mar 13, 2005 4:10 pm
Posts: 7519
Location: Canada
moved. good info. I have tried the silver on a sample and found it workedfine. I continue to use the regular material.

_________________
Stephen
Web: www.trinityamps.com. Facebook: facebook.com/trinityamps. Twitter: @trinityamps


Top
 Profile  
 
 Post subject:
PostPosted: Fri Apr 25, 2008 3:33 pm 
Offline
Experienced
Experienced

Joined: Fri Mar 14, 2008 12:05 pm
Posts: 432
Location: Massachusetts
I wanted to add a quick solder "factoid" that I just learned this past fall. This would affect anyone who is an occasional solderer at home like myself...

The flux in solder has an expiration date, as does liquid flux in those gallon jugs or flux pens used for rework!!! This came as a real shock to me and at first I thought it was a ploy by the solder and flux manufacturers to sell more solder and flux. After thinking about however, it explained why I could solder great at work but not so great at home. Solder which contains flux looses it's effectiveness in about two years, and flux in liquid form at about one year, I'm thinking because it's more exposed to the air and the "good stuff" must evaporate out of it. Something to think about if your soldering skills seem to have gone down "the tubes" over the years! Sorry :wink:

Joe G

_________________
Some assembly required,
Brain sold separately...


Top
 Profile  
 
 Post subject:
PostPosted: Tue Apr 29, 2008 1:40 pm 
Offline
Expert
Expert

Joined: Tue Sep 19, 2006 11:46 am
Posts: 1078
Location: PA
I don't know. I really like my 44 Kester

I didn't know about the 2 yr limit on solder, that's new.


Top
 Profile  
 
 Post subject:
PostPosted: Tue Apr 29, 2008 3:02 pm 
Offline
Experienced
Experienced

Joined: Fri Mar 14, 2008 12:05 pm
Posts: 432
Location: Massachusetts
Kester "44" is a good choice. The flux is a bit aggressive (highly active type RA) but supposedly the residue is non-corrosive and should be fine if left uncleaned. The flux residue should be removed if the end product will see warm/humid climates or environments as the flux residue can become reactivated and corrode the solder joints over time. I'm sure flux looses it's "potency" (it's ability to pre-clean the ares to be soldered) over time, but the 2 year expiration time frame may be a military requirement. If your solder flows and "wets" nicely, looks bright and shiny when done, I would say your good!

Joe G

_________________
Some assembly required,
Brain sold separately...


Top
 Profile  
 
 Post subject:
PostPosted: Thu Jun 19, 2008 4:26 pm 
Offline
Expert
Expert

Joined: Tue Sep 19, 2006 11:46 am
Posts: 1078
Location: PA
Hey Joey,
I was wondering if you know of a cheaper, better solder to go with. And why (gotta know).
Just curious.
Thanks :D


Top
 Profile  
 
 Post subject:
PostPosted: Thu Jun 19, 2008 6:49 pm 
Offline
Experienced
Experienced

Joined: Fri Mar 14, 2008 12:05 pm
Posts: 432
Location: Massachusetts
I know what you mean... $25+ a pound for solder. Our government contracts specify 63/37, RMA flux solder (I would use the .031" size for our purposes) because of the very rapid transition from solid to liquid and back to solid. This ratio has to be the fastest recovering solder that I've used, and I actually watch it under a microscope while I'm soldering. We've been using Kester™ almost exclusively, but have also had Alpha Metals™ in the past. We buy it with your taxes so price is no object! When I get into work tomorrow I can check into it further.
Do you just need enough for one project or do you plan to stock up? Let me see what I can do...

Joe G

_________________
Some assembly required,
Brain sold separately...


Top
 Profile  
 
 Post subject:
PostPosted: Fri Jun 20, 2008 12:10 am 
Offline
Expert
Expert

Joined: Tue Sep 19, 2006 11:46 am
Posts: 1078
Location: PA
I usually buy the pound rolls. So whatever you come up with. Faster recovery sounds great. Appreciate the info, I'll run with what you come up with.
Later :D :D


Top
 Profile  
 
Display posts from previous:  Sort by  
Post new topic Reply to topic  [ 25 posts ]  Go to page 1, 2  Next

All times are UTC - 5 hours [ DST ]


Who is online

Users browsing this forum: No registered users and 29 guests


You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot post attachments in this forum

Search for:
Jump to:  
cron
Powered by phpBB® Forum Software © phpBB Group